Semiconductor circuit arrangement with trench isolation and fabrication method

ABSTRACT

An explanation is given of, inter alia, a circuit arrangement containing a trench which penetrates through a charge-storing layer ( 18 ) and a doped semiconductor layer ( 14 ). The trench simultaneously fulfils a multiplicity of functions, namely an insulating function between adjacent components, the patterning of the charge-storing layer and also the subdivision of doping layers of the semiconductor layer ( 14 ).

The invention relates to a semiconductor circuit arrangement having asubstrate, which carries in the order specified:

-   -   a doped semiconductor layer of a first conductivity type or        conduction type,    -   an electrically insulating layer,    -   and an electrically conductive or an electrically insulating        charge-storing layer, which is suitable for the storage of        charges.

Moreover, the semiconductor circuit arrangement contains at least onetrench which penetrates through the charge-storing layer and alsoextends into the doped semiconductor layer.

The substrate is for example a wafer made of a semiconductor material,e.g. made of silicon. The layer suitable for the storage of charges isalso referred to as floating gate particularly in the case of circuitarrangements having memory cells.

It is an object of the invention to specify an integrated circuitarrangement which is simple to fabricate and simple to drive and, inparticular, has very good electrical properties. In particular, theintention is to specify a circuit arrangement having a multiplicity ofmemory cells. Moreover, the invention relates to a method which can beused, in particular, to fabricate the semiconductor circuit arrangement.

The object related to the circuit arrangement is achieved by means of acircuit arrangement having the features of patent claim 1. Developmentsare specified in the subclaims.

The invention is based on the consideration that there are in principletwo possibilities for fabricating the trench. Thus, it is possible tofabricate the trench, apart from auxiliary layers which are completelyremoved again after the formation of the trench, before the applicationof layers which remain in the circuit arrangement, so that the trenchdoes not penetrate through these layers. On the other hand, it ispossible to introduce the trench only after layers which remain in thecircuit arrangement have been applied to the substrate, so that thetrench penetrates through these layers.

The invention is furthermore based on the consideration that theproduction of the trench after the application of layers which remain inthe circuit arrangement simultaneously permits the patterning of theselayers and the orientation of the trench with respect to the patternedregions, i.e. a so-called self-alignment. However, it is possible forthe trench to be assigned further functions in the integrated circuitarrangement. In the circuit arrangement according to the invention, thetrench also serves, moreover, for subdividing the doped semiconductorlayer. This requires the trench to be deeper than the thickness of thedoped semiconductor layer. Thus, in the circuit arrangement according tothe invention, the trench also has, besides the insulating function forinsulating adjacent components, two further functions, namely:

-   -   the patterning of the charge-storing layer, and    -   the patterning and insulation of the doped semiconductor layer.

In one refinement, the circuit arrangement contains a plurality oftrenches arranged next to one another, for example trenches lyingparallel to one another.

Arranged between the trenches are in each case a multiplicity of memorycells, in particular EEPROM memory cells or flash EEPROM memory cells(Electrically Erasable Programmable Read Only Memory). In a nextrefinement, the charge-storing layer is subdivided into charge-storingregions transversely with respect to the direction in which the trencheslie.

In one development of the circuit arrangement, a doped semiconductorlayer having a conductivity type opposite to the first conductivity typeis arranged between the doped semiconductor layer and the substrate. Thetrench also penetrates through the semiconductor layer of oppositeconduction type and extends into the substrate. The subdivision of adoped semiconductor layer by means of two trenches, e.g. in theso-called bit line direction, already leads to a multiplicity ofadvantages with regard to the operation of the memory cells. By way ofexample, memory cells can be selectively erased. The demarcation of afurther lower semiconductor layer lying below the upper semiconductorlayer with the aid of the trenches leads to a further improvement of theelectrical properties. By way of example, there is a reduction in thejunction capacitance between the two semiconductor layers for eachindividual bit line. Furthermore, additional options are afforded forthe electrical driving of the components.

In an alternative development with two additional semiconductor layers,the trench ends, by contrast, in the semiconductor layer of oppositeconduction type, so that only the semiconductor layer of the firstconduction type is separated by the trenches. This measure is sufficientfor many applications and simpler to carry out than severing both ormore than two semiconductor layers with the aid of the trenches.

In one refinement, the substrate is a semiconductor substrate whichpreferably contains silicon or comprises silicon. The silicon is weaklypredoped, for example. In another refinement, the doped semiconductorlayer forms the channel region of a transistor or the channel regions ofa multiplicity of transistors. In a next refinement, the firstconductivity type is the p conductivity type, i.e. electrical conductionthrough defect electrons or so-called holes. In an alternativerefinement, the first conductivity type is the n conductivity type, i.e.electrical conduction through conduction electrons.

In a next refinement, the electrically insulating layer contains anoxide or comprises an oxide, in particular a silicon dioxide which ispreferably thermally produced or deposited. During the programming anderasure of the memory cells, charge carriers tunnel through or surmountthe electrically insulating layer adjoining the substrate. Duringprogramming, e.g. electrons or electron holes are stored in thecharge-storing layer. Charge carriers, which are also referred to as hotcarriers in this context, are accelerated during programming and/orerasure on account of an electric field in such a way that they cansurmount an energy barrier between the charge-storing layer and thesubstrate. As an alternative, by the application of a suitable potentialgradient, the energy barrier may be reduced in such a way that chargecarriers can tunnel through it.

In a next refinement, the charge-storing layer contains polycrystallinesilicon or comprises polycrystalline silicon, preferably dopedpolycrystalline silicon. In an alternative refinement, thecharge-storing layer contains a nonmetal nitride or comprises a nonmetalnitride, in particular silicon nitride. In another alterativerefinement, the charge-storing layer contains another material which isable to bind charge carriers for example in material defects such as,for example, aluminum oxide or hafnium oxide.

In one development of the circuit arrangement according to theinvention, an electrically conductive layer is provided, which ispatterned as word lines. A further electrically insulating layer isarranged between the electrically conductive layer and thecharge-storing layer. In one refinement, the trench or the trencheswhich extend into the semiconductor layer do not penetrate through saidelectrically conductive layer and said electrically insulating layer.

In one refinement, the electrically conductive layer contains apolycrystalline material or a metal. By way of example, the electricallyconductive layer comprises polycrystalline silicon, in particular dopedpolycrystalline silicon. In a next refinement, the electricallyconductive layer is subdivided into strips lying transversely or at anangle of 90 degrees with respect to the trenches. In another refinement,the electrically conductive layer has subdivisions at locations at whichthe charge-storing layer is also subdivided, that is to say that the twolayers have been patterned using the same mask.

In one development of the circuit arrangement, there is at least onetrench, which is shallower and wider in comparison with the trenchpenetrating through the electrically insulating layer and which isarranged in the semiconductor layer of the first conductivity type andthrough which penetrates the deep trench penetrating through theelectrically insulating layer. This measure, without relatively highprocess-technological outlay, results in degrees of freedom for themethod implementation, because the shallow trench can be used asadditional insulation. The process-technological additional outlay islow because shallow trenches have to be produced anyway in many circuitarrangements. In particular, shallow trenches are used in logiccircuits. Shallow trenches typically have a depth of less than 500 nm(nanometers). By contrast, the deep trench has a depth of greater than700 nm, greater than 1 μm (micrometer) or even greater than 1.5 μm. Thedepth of the deep trench depends, in particular, on the voltageconditions, because the latter in turn determine the thickness of thedoped semiconductor layers which are intended to be subdivided by thedeep trenches parallel to the bit lines.

In a next development of the circuit arrangement, the shallow trenchdoes not penetrate through the charge-storing layer and/or theelectrically insulating layer. Thus, the shallow trench must have beenfabricated, and in particular also filled, before the application ofthese two layers. This means that shallow trench and deep trench areprocessed independently of one another. In particular, the depths of thedifferent types of trench can be defined and optimized independently ofone another. Furthermore, this method procedure avoids problems whicharise on account of the major height differences in the case of thesimultaneous filling of shallow trenches and deep trenches in the caseof the subsequent leveling of the surface.

In one development, the shallow trench is completely filled with anelectrically insulating material or the shallow trench contains anelectrically insulating material, for example silicon dioxide. In a nextdevelopment, the shallow trench projects symmetrically beyond the deeptrench, so that the insulation properties are equally good in aplurality of directions.

In a next development, there is at least one further shallow trenchthrough which no trench, in particular no deep trench, penetrates. In anext development, the shallow trench through which the deep trenchpenetrates lies in a memory cell array and the shallow trench throughwhich a trench does not penetrate lies in a logic circuit arrangement inwhich, by way of example, basic logic functions are produced, e.g. NANDswitching functions. The logic circuit is e.g. part of a monolithiccircuit which also contains a memory cell array having deep trenches.

In a next development, the electrically conductive layer through whichthe deep trench does not penetrate and/or the electrically insulatinglayer through which the deep trench does not penetrate are at leastpartly arranged in the shallow trench. This measure makes it possible tointroduce a cutout into the electrically conductive layer through whichthe deep trench does not penetrate, without stringent requirements beingmade of its depth. All that is important is that the electricallyconductive layer is completely interrupted. There is a relatively largeleeway, for example of more than 10 nm or more than 20 nm, for theprojection of the cutout into the shallow trench. Despite differentdepths, it is ensured that the coupling factor between the capacitanceof the charge-storing layer and the electrically conductive layer isrelatively independent of the depth if the cutout lies within the trenchedges of the shallow trench.

In a next development of the circuit arrangement, the circuitarrangement contains a further charge-storing layer, which adjoins thecharge-storing layer and, in one refinement, comprises the samematerial. At least one cutout is arranged in the further charge-storinglayer, the bottom of said cutout preferably lying completely within theedge of the deep trench or of the shallow trench. The depth of saidcutout is also noncritical provided that the further charge-storinglayer is completely patterned. The same relationships as explained inthe previous paragraph hold true with regard to the coupling factor ofthe capacitances.

In another development, the trench is filled with an electricallyinsulating material or the trench contains an electrically insulatingmaterial. In particular, oxides such as silicon dioxide, for example,are suitable for filling the trench. In a next development, the trenchcontains an electrically conductive or electrically semiconductingmaterial insulated from the trench wall, for example a polycrystallinematerial, in particular polycrystalline silicon, which is doped orundoped.

The invention relates, moreover, to a method for fabricating asemiconductor circuit arrangement, in particular for fabricating thecircuit arrangement according to the invention or one of itsdevelopments. Thus, the technical effects mentioned above also hold truefor the method.

In one development of the method according to the invention, a hard masklayer is used for introducing the deep trench. The hard mask layer canbe removed before the trench is filled. However, the hard mask layer canalso be removed only after the trench has been filled with a fillingmaterial and the filling material has subsequently been etched back.What is achieved by this measure is that, during the etching-back,layers lying below the hard mask are protected by the hard mask.

Exemplary embodiments of the invention are explained below withreference to the accompanying drawings, in which:

FIGS. 1A to 1F show fabrication stages in accordance with a first methodvariant with a hard mask layer which is removed directly after thefabrication of deep trenches,

FIG. 2 shows a fabrication stage in accordance with a second methodvariant with a hard mask layer which is utilized over a plurality ofmethod steps,

FIGS. 3A and 3B show fabrication stages in accordance with a thirdmethod variant with shallow trenches through which deep trenchespenetrate, and

FIGS. 4A and 4B show fabrication stages in accordance with a furthermethod variant with a floating gate double layer.

FIG. 1A shows a weakly p-doped semiconductor substrate 10 made ofsilicon. An n-doped semiconductor layer has been introduced into thesemiconductor substrate 10 by doping, said layer lying for example at adepth of 800 nm to 1.6 μm (micrometers). Moreover, a p-dopedsemiconductor layer 14 has been produced in the semiconductor substrate10, said layer extending from the surface of the semiconductor substratedown to a depth of about 800 nm. At the edges of a cell array, thesemiconductor layers 12 and 14 may be formed as a well, that is to saythat they are taken as far as the surface of the semiconductor substrate10. However, other contact-making possibilities, too, are utilized inanother exemplary embodiment.

By way of example, the dopings of the semiconductor layers 12 and 14 arefabricated by implantation. Semiconductor layers 12 and 14 formed inwell-type fashion are also referred to as n-well or as p-well.

An oxide layer 16 is subsequently applied, for example thermally, saidlayer having a thickness of 6 to 15 nm, for example. A floating gatelayer 18 is then deposited on the oxide layer 16, said floating gatelayer comprising in-situ-doped polycrystalline silicon, and having athickness of 50 to 150 nm, for example.

In a subsequent method step, a hard mask layer 20, for example a TEOSlayer (Tetra Ethyl Ortho Silicate) having a thickness of hundreds of nm,is applied on the floating gate layer 18. The thickness depends on theselectivity of the trench etching. In other words, given a highlyselective etching or another hard mask material, the thickness may alsobe thinner, under certain circumstances.

As illustrated in FIG. 1B, firstly the hard mask layer 20 is patternedwith the aid of a lithography method and a photomask (not illustrated),a cutout 30 arising firstly only in the hard mask layer 20. During thefabrication of the cutout 30, etching is effected for example in atime-controlled manner. The photoresist is removed after the patterningof the hard mask layer 20. Afterward, with the aid of the patterned hardmask layer 20, the cutout 30 is extended to form a trench 32 having adepth of about 1.8 μm, for example, measured from the boundary betweenhard mask layer 20 and floating gate layer 18. By way of example, areactive ion etching RIE is carried out for the etching of the trench32. The trench 32 has a width of 200 nm, for example. The hard masklayer 20 is already thinned to a great extent during the etching of thetrench 32, so that only an etching reserve of 100 nm, for example,remains.

As illustrated in FIG. 1C, the hard mask layer 20 is subsequentlyremoved or etched away. Afterward, a so-called liner oxidation iscarried out, during which an oxide layer 40 having a thickness of 40 nm,for example, is produced at the wall of the trench 32 and on thefloating gate layer 18. After the production of the liner oxide layer40, a polycrystalline silicon layer 42 is deposited, which completelyfills the trench 32. By way of example, a low-pressure CVD method(Chemical Vapor Deposition) is utilized for the deposition of thesilicon layer 42. In the exemplary embodiment, the polycrystallinesilicon layer 42 is undoped. In another exemplary embodiment, however, adoped polycrystalline silicon layer 42 is fabricated.

As illustrated in FIG. 1D, regions of the silicon layer 42 which lieoutside the trench 32 are subsequently removed, for example with the aidof a reactive ion etching method. Moreover, in the upper region of thetrench 32, the silicon layer 42 is removed selectively with regard tothe oxide layer 40, for example down to a depth of 300 nm below theboundary between oxide layer 16 and p-doped semiconductor layer 14.After the etching of the silicon layer 42, an insulating fillingmaterial 50 is introduced into the upper part of the trench 32, forexample silicon dioxide with the aid of an HDP method (High DensityPlasma). An oxide layer 50 is produced in the upper region of the trench32 and on the floating gate layer 18.

As illustrated in FIG. 1E, the oxide layer 50 is subsequently etchedback over the whole area, a cutout 60 arising in the upper region of thetrench 32. The etching-back of the oxide layer 50 is carried out forexample with the aid of an RIE method (reactive ion etching) or with theaid of a wet etching. The bottom of the cutout 60 should not lie belowthe boundary between oxide layer 16 and p-doped semiconductor layer 14.

As shown in FIG. 1F, a dielectric layer 70 is subsequently deposited,for example an ONO layer (Oxide-Nitride-Oxide). The dielectric layer 70has a thickness of less than 20 nm, for example. After the applicationof the dielectric layer 70, a control gate layer 72 is applied, forexample made of in-situ-doped polycrystalline silicon and having athickness of e.g. greater than 100 nm.

In subsequent method steps (not illustrated), the control gate layer 72,the dielectric layer 70 and the floating gate layer 18 are patternedsimultaneously in a word line direction, which lies parallel to thesheet plane, see arrow 74. A bit line direction lies perpendicular tothe sheet plane and corresponds to the direction of the trench 32. Afterthe patterning of the control gate layer 72, channel and source regionsare introduced into the p-doped semiconductor layer 14 by doping, saidregions lying in front of and behind the sheet plane, respectively, withreference to FIG. 1F. One or a plurality of metallization layers formaking contact with the memory cells are applied in further methodsteps. Finally, a memory circuit 76 is completed, containing thearrangement illustrated in FIG. 1F.

FIG. 2 shows a fabrication stage in accordance with a second method, inwhich a hard mask layer 20 a is used over a plurality of method steps.Proceeding from a semiconductor substrate 10 a, the method stepspresented above with reference to FIGS. 1A and 1B are performed forproducing an n-doped semiconductor layer 12 a, a p-doped semiconductorlayer 14 a, an oxide layer 16 a and a floating gate layer 18 a.Reference is made to FIGS. 1A to 1B with regard to the details.Afterward, the hard mask layer 20 a is applied and patterned with theaid of a photolithographic method, the floating gate layer 18 ainitially remaining unpatterned. After the removal of the photoresist,the patterned hard mask layer 20 a is used for producing a trench 32 ahaving the same properties as the trench 32.

With the hard mask layer 20 a still present on the oxide layer 18 a, afor example thermal liner oxidation is subsequently carried out forproducing an oxide layer 40 a situated at the walls of the trench 32 aand on the hard mask layer 20 a.

In a next method step, a doped or undoped polycrystalline silicon layer42 a is deposited, which completely fills the trench 32 a. Afterward,the polycrystalline silicon layer 42 a is etched back for example withthe aid of a reactive ion etching method, the silicon layer 42 a beingremoved outside the trench 32 a and in the upper region thereof. Thoseregions of the oxide layer 40 a which lie on the hard mask layer 20 aare also removed in this case. The hard mask layer 20 a protects thefloating gate layer 18 a during the etching-back.

The hard mask layer 20 a is removed after the etching-back. Afterward,further processing is effected in the manner explained above withreference to FIGS. 1D to 1F, i.e. application of an oxide layercorresponding to the oxide layer 50, etc.

FIGS. 3A and 3B show fabrication stages in accordance with a thirdmethod variant, in which a deep trench 32 b penetrates through a shallowtrench 100. The shallow trench 100 is produced in a semiconductorsubstrate 10 b, corresponding to the semiconductor substrate 10, beforeor after the application of an oxide layer 16 b, corresponding to theoxide layer 16, and a floating gate layer 18 b, corresponding to thefloating gate layer 18, for example before the implantation forproducing an n-doped semiconductor layer 12 b or a p-doped semiconductorlayer 14 b. Except for the introduction of the trench 100, the methodsteps explained with reference to FIGS. 1A to 1D are performedunchanged, see broken line 100 in said figures. When the stateillustrated in FIG. 1D is reached, an oxide layer corresponding to theoxide layer 50 is etched back, a cutout 60 b arising in the upper regionof the trench 32 b. During the etching-back, it is not critical if thebottom of the cutout 60 b lies below the boundary between the oxidelayer 16 b and the semiconductor layer 14 b. By way of example, it ispossible to etch into the shallow trench 100 to an extent of tens of nm,see broken line 102. The trench 100 is filled with an insulatingmaterial, for example with silicon dioxide. This insulating material,even with the bottom of the cutout 60 b lying at a deeper level, affordsa sufficient insulation between the subsequently applied control gateand the semiconductor layer 14 b.

This is because the trench 100 has a larger width than the trench 32 b.In the exemplary embodiment, the shallow trench 100 has a width of 300nm and a depth of 400 nm. Given a symmetrical arrangement of the deeptrench 32 b with respect to the shallow trench 100, the shallow trench100 projects beyond the deep trench 32 b by a distance A of 50 nm oneach side. The larger width of the trench 100 also prevents instances ofincipient etching of the tunnel oxide 16 b in edge regions of the trench100 during the etching of the cutout 60 b, see regions 104 and 106,which leads to a higher reliability.

As illustrated in FIG. 3B, a dielectric layer 70 b, corresponding to thedielectric layer 70, is subsequently applied. A control gate layer 72 b,corresponding to the control gate layer 72, is then applied. The othermethod steps explained with reference to FIG. 1F are subsequentlyperformed.

The method with a shallow trench through which a deep trench penetratesis carried out, in accordance with a fourth method variant, also in thecase of the method variant explained with reference to FIG. 2, seebroken line 100 in FIG. 2. That is to say that a hard mask layercorresponding to the hard mask layer 20 a can be utilized for aplurality of method steps even when a deep trench corresponding to thedeep trench 32 a penetrates through the shallow trench 100.

FIGS. 4A to 4B show a fifth method variant, in which a floating gatedouble layer comprising a floating gate layer 18 c, corresponding to thefloating gate layer 18, and a floating gate layer 110 is fabricated. Themethod steps up to the etching-back of an oxide layer 50 c correspondingto the oxide layer 50 are the same as explained above with reference toFIGS. 1A to 1D. For a semiconductor substrate 10 c, an n-dopedsemiconductor layer 12 c, a p-doped semiconductor layer 14 c, an oxidelayer 16 c, a trench 32 c, an oxide layer 40 c and a polycrystallinesilicon trench filling 42 c, reference is made to the explanations withrespect to FIGS. 1A to 1D.

In a departure from the method explained with reference to FIG. 1D, theoxide layer 50 c is etched back only as far as the floating gate layer18 c, the floating gate layer 18 c serving as an etching stop layer. Thetrench 32 c thus remains filled with the oxide layer 50 c in its upperregion as well.

This procedure, as also explained with reference to FIG. 3A, preventsdamage to the thin oxide of the oxide layer 16 c at the edges 112 and114 of the trench 32 c during the etching-back of the oxide layer.

The floating gate layer 110 is then deposited, for examplepolycrystalline silicon, which is doped in situ.

As illustrated in FIG. 4B, the floating gate layer 110 is then patternedwith the aid of a photolithographic method. In this case, a cutout 120is produced above the trench 32 c, the width of said cutout being lessthan the width of the trench 32 c. The cutout 120 is orientedsymmetrically with respect to the trench center of the trench 32 c.During the etching of the cutout 120, care has to be taken only toensure that the floating gate layer 110 is completely severed. Anoveretching is not critical, because the bottom of the cutout 120 issurrounded on all sides by that part of the oxide layer 50 c whichremains in the trench 32 c, see broken line 122. Even when the bottom ofthe cutout 120 is in a different position, there is only aninsignificant change in a coupling factor of the capacitances betweenthe floating gate and the control gate of the memory cells to befabricated on account of the projection of the floating gate layer 110over the floating gate layer 18 c.

Afterward, the method steps explained above with reference to FIG. 1Fare carried out. Instead of a three-layer ONO layer, it is also possibleto use a single-layer dielectric layer.

In accordance with a sixth method variant, the methods in accordancewith FIG. 2 and in accordance with FIGS. 4A and 4B are combined, so thatthe hard mask is utilized for a plurality of method steps even in amethod in which a floating gate double layer is produced. Theetching-back of the oxide layer is then carried out e.g. in atime-controlled manner. The hard mask is then removed.

The cutout 120 can also be made wider than the trench 32 c. On the basisof the two lithography methods for the two floating gate layers 18 c and110, the width of the trench 32 c and the width of the cutout 120 can bechosen independently of one another.

In other exemplary embodiments, a CMP method (Chemical MechanicalPolishing) is also used instead of etching-back. Instead of a hard masklayer made of TEOS, it is also possible to use a hard mask layer made ofanother material, for example made of a nitride such as silicon nitride.If the deep trench has a smaller depth than in the exemplaryembodiments, a photoresist layer may also be used instead of the hardmask.

Consequently, a plurality of variants for fabricating nonvolatile memorycells has been explained, in which:

-   -   deep isolation trenches are used for flash EEPROM memory cells        or for simple EEPROM memory cells,    -   method sections, i.e. so-called modules, for fabricating shallow        isolation trenches (STI—Shallow Trench Isolation) and modules        for fabricating and filling deep trenches (DTI—Deep Trench        Isolation) can be carried out in a simple manner, in particular        successively, in a fabrication process, and    -   the problems of “classic” integration, in which deep trenches        and shallow trenches are fabricated at the start of the method,        are avoided. In particular, no problems arise during the        planarization of HDP oxide fillings (High Density Plasma) which        have a different height above the shallow trenches and the deep        trenches.

In the exemplary embodiments explained, deep trench isolations lead toinsulated well strips. The trenches in the memory cell array have alarger depth than trenches in the drive circuit of the memory array orin a logic circuit applied on the same chip. On account of the fillingwith polycrystalline silicon, it is possible to fabricate deep trencheshaving a small ratio of width to depth, e.g. with ratios smaller than ¼or {fraction (1/10)}.

The methods explained are suitable in particular for memory cells basedon a cell concept in which the charges are applied to the floating gateor are removed from the floating gate on the basis of theFowler-Nordheim tunnel effect.

The variant with a deep trench through which no shallow trenchpenetrates makes it possible:

-   -   to manage with a small chip area for the insulation,    -   to avoid problems of alignment between shallow trenches and deep        trenches, so that no additional tolerances have to be provided,        and    -   to planarize shallow trenches lying outside the cell array        without any problems.

The variant with a deep trench through which a shallow trench penetratesmakes it possible:

-   -   to improve the insulation between control gate and substrate or        p-doped region,    -   to achieve larger coupling factors on account of the reduced        coupling of floating gate and substrate,    -   to be able to set the coupling factor better, and    -   to be able to etch back the filling oxide of the trench more        easily.

Both variants make it possible:

-   -   to avoid additional CMP steps (Chemical Mechanical Polishing),    -   to avoid a CMP method with major height differences, and    -   to carry out and to optimize processes for fabricating the        shallow trenches independently of processes for fabricating the        deep trenches.

The methods explained make it possible, in particular, to avoid orreduce damage to the sensitive tunnel oxide in particular at the edgesof the trenches, so that the yield and reliability increase. Moreover,it is thus possible to produce strips made from the doped wells in asimple manner, said strips running in the bit line direction.

In other exemplary embodiments, the same structures are fabricated basedon other doping layer sequences, e.g. p-substrate and n-well. Analternative is to work with n-substrate and p-well. A third alternativeworks with n-substrate and p-well and also n-well.

1-20. (Cancelled).
 21. A semiconductor circuit arrangement on asubstrate comprising: a doped semiconductor layer having a firstconductivity type disposed on the substrate; an insulating layerdisposed on the doped semiconductor layer; a charge storing layerconfigured for storing an electrical charge disposed on the insulatinglayer; and at least one deep trench that penetrates through the chargestoring layer and extends into the doped semiconductor layer.
 22. Thesemiconductor circuit arrangement of claim 21, where the charge storinglayer is a conducting layer.
 23. The semiconductor circuit arrangementof claim 21, where the charge storing layer is an insulating layer. 24.The semiconductor circuit arrangement of claim 21, where the at leastone deep trench penetrates through the doped semiconductor layer intothe substrate.
 25. The semiconductor circuit arrangement of claim 21,further comprising a second doped semiconductor layer having a secondconductivity type disposed between the substrate and the dopedsemiconductor layer, where the second conductivity type is opposite tothe conductivity type of the doped semiconductor layer.
 26. Thesemiconductor circuit arrangement of claim 25, further comprising the atleast one deep trench penetrating through the doped semiconductor layerand extending into the second doped layer.
 27. The semiconductor circuitarrangement of claim 25, further comprising the at least one deep trenchpenetrating through the doped semiconductor layer and the secondsemiconductor layer into the substrate.
 28. The semiconductor circuitarrangement of claim 21, further comprising a conductive layer and asecond insulating layer where the second insulating layer is disposed onthe charge storing layer and the conductive layer is disposed on thesecond insulating layer.
 29. The semiconductor circuit arrangement ofclaim 21, further comprising a shallow trench that is arranged in thedoped semiconductor layer.
 30. The semiconductor circuit arrangement ofclaim 29, where the shallow trench does not penetrate through the chargestoring layer and the insulating layer and the shallow trench extendsabout laterally symmetrical in all directions beyond an edge of the deeptrench.
 31. The semiconductor circuit arrangement of claim 30, where theshallow trench extends laterally about 50 nm beyond the edge of the deeptrench.
 32. The semiconductor circuit arrangement of claim 29, where theshallow trench contains an insulating material.
 33. The semiconductorcircuit arrangement of claim 32, where the insulating material ispolycrystalline silicon.
 34. The semiconductor circuit arrangement ofclaim 29, further comprising at least one shallow trench through whichno deep trench penetrates.
 35. The semiconductor circuit arrangement ofclaim 34, where the semiconductor arrangement forms a logic circuitarrangement.
 36. The semiconductor circuit arrangement of claim 29,further comprising at least one shallow trench having the same depth asthe deep trench.
 37. The semiconductor circuit arrangement of claim 29,further comprising at least one shallow trench where the deep trenchpenetrates through the bottom of the shallow trench.
 38. Thesemiconductor circuit arrangement of claim 37, where the semiconductorarrangement is a memory circuit arrangement.
 39. The semiconductorcircuit arrangement of claim 29, where the electrically conductive layerextends at least partly over the shallow trench.
 40. The semiconductorcircuit arrangement of claim 29, where the second electrically insultinglayer extends at least partly over the shallow trench.
 41. Thesemiconductor circuit arrangement of claim 21, further comprising asecond charge storing layer disposed on the charge storing layer and thedeep trench does not penetrate into the second charge storing layer. 42.The semiconductor circuit arrangement of claim 41, further comprising anopening in the second charge storing layer above the deep trench. 43.The semiconductor circuit arrangement of claim 42, where the edges ofthe opening are a smaller distance apart than the lateral edges of thedeep trench.
 44. The semiconductor circuit arrangement of claim 21,further comprising an insulating material that fills the deep trench.45. The semiconductor circuit arrangement of claim 21, furthercomprising an insulating material disposed on the wall of the trench.46. The semiconductor circuit arrangement of claim 45, wherein theelectrically insulating material on the wall of the trench is silicondioxide.
 47. The semiconductor circuit arrangement of claim 45, wherethe trench is filled with an electrically conductive or semi-conductivematerial and the material is isolated from the trench wall with theelectrically insulating material.
 48. The semiconductor circuitarrangement of claim 47, wherein the conductive or semi-conductivematerial is polysilicon.
 49. The semiconductor circuit arrangement ofclaim 21, further comprising a plurality of deep trenches each deeptrench arranged next to one another in a transverse direction separatinga plurality of charge storing layers arranged in the transversedirection.
 50. The semiconductor circuit arrangement of claim 49,wherein the plurality of deep trenches separate a plurality of memorycells arranged in the transverse direction, the combination of whichforms a memory circuit.
 51. The semiconductor circuit arrangement ofclaim 50, wherein the plurality of memory cells form EEPROM memory cellsor EEPROM flash memory cells.
 52. A method for fabricating asemiconductor circuit arrangement comprising: forming a dopedsemiconductor layer of a first conductivity type; disposing anelectrically insulating layer on the doped semiconductor layer;disposing a charge storing layer on the electrically insulating layer;and forming a deep trench that penetrates through the charge storinglayer, the insulating layer and into the semiconductor layer.
 53. Themethod of claim 52, further comprising disposing a mask on the chargestorage layer; and forming the trench using the mask layer as aprotection for the charge storage layer.
 54. The method of claim 53,where the mask is a photoresist.
 55. The method of claim 53, where themask is a hard mask layer.
 56. The method of claim 55, where the hardmask material is TEOS.
 57. The method of claim 53, further comprising:filling the deep trench with a filling material; and etching back thefilling material.
 58. The method of claim 57, further comprisingremoving the mask after forming the trench and before filling the trenchwith the filling material.
 59. The method of claim 57, furthercomprising forming an oxide liner on the inner wall of the trench wherethe oxide liner is formed before filling the trench.
 60. The method ofclaim 57, where the etching back includes a CMP process.
 61. The methodof claim 57, further comprising: etching back the filling material sothat a region uncovered during the etching back process extends into aregion where the semiconductor layer was formed; and filling theuncovered region with a second filling material.
 62. The method of claim61, wherein the second filling material is an oxide.
 63. The method ofclaim 52, further comprising: forming a shallow trench in the dopedsemiconductor layer where the shallow trench is shallower and wider thanthe first trench; filling the shallow trench with a third fillingmaterial; and planarizing the filling material in the shallow trench,wherein the forming, filling and planarizing steps are performed beforedisposing the charge-storing layer.
 64. The method of claim 63, where atleast one shallow trench is arranged in a region where the deep trenchpenetrates the shallow trench.
 65. The method of claim 63, wherein atleast one shallow trench is arranged in a region where the deep trenchdoes not penetrate the shallow trench.
 66. The method claim 63, furthercomprising etching the third filling material such that the regionuncovered during the etching extends into a region where thesemiconductor layer was formed.
 67. The method of claim 66, furthercomprising further filling the uncovered region with an insulatingmaterial.
 68. The method of claim 66, further comprising further fillingthe uncovered region with a conducting material.
 69. The method of claim63, further comprising: disposing at least one further conductingcharge-storing layer adjoining the charge-storing layer; and patterningthe further charge-storing layer, where the patterning of the furthercharge storing layer forms a cutout that extends into the trench. 70.The method of claim 69, where the patterning is performed beforedisposing further layers on the further charge-storing layer.
 71. Themethod of claim 63, further comprising: disposing a further insulatingcharge storing layer adjoining the charge-storing layer; and patterningthe further charge storing layer, where the patterning of the furthercharge storing layer forms a cutout that extends into the deep trench.72. The method of claim 71, where the patterning is performed beforeapplying further layers on the further charge-storing layer.